Introduction to products
PRODUCT NAME SLE06 Zinc Silicate Epoxy Primer
BRIEF Two Pack liquid and powder antirust paint made from inorganic water silicate as base, zinc powder and additive.
FEATURES
-Zero VOC, No flash point, No public nuisance, No pollution
-Excellent lone-term heavy-duty anticorrosive coating,
-Excellent heat resistance, up to Continuous 400℃ and moment 600℃
-Welding and Cutting is allowed, electrical conductivity, radiation resistance,
resistance to ultraviolet light
-Excellent cathodic protection
-Cutting and Welding is allowed as shop primer
RESISTANCE GUIDE
HEAT RESISTANCE Up to 400℃ dry heat
WEATHERABILITY Severe conditions
SOLVENTS Resists arene solvents, most petroleum solvents and crude oil
ACIDS Suitable for splash and spillage to mild acids when suitably coated
ALKALIS Do not use in strong alkaline conditions unless suitably topcoated
SALTS Suitable for immersion when suitably coated
WATER Suitably for immersion in fresh and salt water when suitably topcoated
ABRASION Very good
USES: Widely used in tank, ships, bridge, offshore facility, wharf, oil equipment, pipeline etc.
TYPICAL PROPERTIES AND APPLICATION DATA
COLOR Gray
DENSITY 2.7g/cm3
SOLIDS BY VOLUME 52%
SOLIDS BY WEIGHT 88%
SPREADING RATE 4.8 m2/kg (40um DFT)
DRYING TIME(23℃) Touch 0.5 Hr Handle 5 Hr
OVERCOAT INTERVAL(23℃) Min 12 Hr Max 7 Days
STORAGE at least 6 months (dry, cool and under cover )
PACKAGING Part A(liquid): 9kg Part B((powder): 21kg
MIXING RATIO (m/m) Add part B to part A slowly, and completely mixed.
Filter the mixer with 100 mesh before using
POT LIFE(23℃) 4 Hr
DIRECTIONS Before using stir or using dynamic mixer mixing two components completely,Just mix a good raw material and mixing of raw materials before can not be together. Rate of cure will vary depending on temperature and other factors such as ventilation, film thickness, humidity, thinner. General thinner isnot necessaries, otherwise Max 5% thinner should be added for needed viscosity after stir. Overmuch thinner will lead sag and slow cure rate, thin film, thinner should be added after mixed. Practical spreading rates may be reduced 5%—25% for wastage of different application conditions.
APPLICATION
STEEL: Round off all rough welds, sharp edges and remove weld spatter. Remove grease, oil and
other contaminants. Steel surface must be prepared by abrasive blast cleaning to ISO Standard Class Sa2.5 or power tool cleaning Class St3.
Don’t apply at temperatures below 5℃ or above 40℃. Don’t apply at relative humidity above 85% or when the surface is less than 3℃ above the dew point.
Don’t apply if there is fog, rain, snow or strong wind.
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-5% with Thinner X-8. Additional coats may be required to attain specified thickness.
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-5% of Thinner X-8 can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-5% of Thinner X-8 can be added.
Over coating: Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants.
CLEAN UP: with Thinner X-8
SAFETY:Pay attention to the safety precautions before and after using this product. Users should comply with the provision of the respective country or local government. It’s dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.